Copper brazing solder no. 94 DIN EN 1044, ISO 3677, B-Cu94P
Copper brazing solder no. 94
SLDR-NO94-(B-CU94P)1KG-D2
Register now and access more than 125,000 products
- For the flux-free soldering of copper/copper connections in oil, gas and liquid gas installations and in heating and drinking water installations with pipe dimensions greater than 28 x 1.5 mm. When soldering brass or red bronze, an additional flux must be used.
- Working temperature: 730°C
- Melting range: 710-880°C
Solder does not contain flux.
Datasheets(X)
Wire diameter x length | 2.0 x 500 mm |
Weight of content | 1 kg |
Min./max. melting temperature | 710 to 880 °C |
Cu composition of the brazing solder (weight-%) | 93.8 % |
P composition of the brazing solder (weight-%) | 6.2 % |
DIN | 8513 |
Material designation | B-Cu94P |
EN standard | 1044 |
Length | 500 mm |
Wire diameter | 2.0 mm |
Min. melting temperature | 710 °C |
Max. melting temperature | 880 °C |
Contains flux | No |
Working temperature | 730 °C |
Product weight (per item) | 1053.000 g |
Last viewed
Pan head tapping screw, C shape with H recessed head DIN 7983, steel, zinc-plated, blue passivated (A2K), shape C, H cross recess
Blade recept. with blade conn. 6.3 x 0.8
Knurled thumb screw, low profile DIN 653, steel 5.8, plain
Round head screw with square neck DIN 603, A2 stainless steel, plain
Textile brush For furniture sliding doors
Countersunk head screw with recessed head, H DIN 965, steel 4.8, zinc-plated, blue passivated (A2K)
Round head screw with square neck and nut DIN 603 with nut, steel, strength class 4.8, zinc-plated, blue passivated
Hexagon head serrated screw with flange W-0274, steel 8.8, zinc-plated, blue passivated (A2K)
pias® drilling screw with hexagon head and drill tip Case-hardened steel, zinc-plated, blue passivated
Powdered chalk